Precipitation behavior and properties of extruded 7136 aluminum alloy under different aging treatments

In this work, the mechanical properties and electrical conductivity of the extruded 7136 aluminum alloy treated by single-stage aging treatment (T6), retrogression and re-aging treatment (RRA), and multiple retrogression and re-aging treatment have been investigated by means of hardness measurements, electrical conductivity tests and tensile tests. The results have shown that the properties of the 7136 alloy such as hardness, tensile strength and electrical conductivity were sensitive to retrogression time (within 90 min). With prolonging the retrogression time, the tensile strength was enhanced first and then decreased, yet the electrical conductivity was continuously increased. The 60 min-treated alloy performed the highest tensile strength (716 MPa), whereas the 90 min-treated alloy possessed the highest electrical conductivity (33.95%IACS). Compared with the T6-treated alloy, the tensile strength and electrical conductivity were improved by 3.3% and 18.9%, respectively. The electrical conductivity showed an obvious increase with repetitious times of the RRA treatment. After 3RRA60 treatment, a good combination of tensile strength (705 MPa) and electrical conductivity (33.20%IACS) can be obtained. Compared with the T6 condition, the tensile strength and electrical conductivity were improved by 1.7% and 16.3%, respectively. The mechanism of microstructure evolution under different aging treatments has been discussed in detail.     

Performance analysis and application on Ti-6Al-4V of micro-forging system

Micro-forging (MF) is a novel surface modification technology which is capable of smoothening and strengthening the workpiece surface simultaneously. Based on analysis of the mechanism and energy conversion of micro-forging process, an electromagnetically driven micro-forging system is developed. To further grasp the kinetic characteristic of the equipment, a simulation model is established and its accuracy is verified. With the help of simulation and experimental results, we propose an input voltage optimization method, which drives the micro-forging head moving in a uniform and stable way. In this study, the influence of MF on surface integrity of Ti-6Al-4V (TC4) is firstly reported. Experimental results show that MF treatment reduces surface roughness (R_a) and increases micro-hardness by 48% and 11.8% at most, respectively. Besides, a compressive stress layer with an amplitude of −1000 MPa and a depth of 0.8 mm is observed. This study analyzes the performance and reveals the potential of micro-forging technology, which lays a solid foundation for expanding its application in TC4 surface modification.     

含金属相变材料温控组件的研究

研究使用一种含有金属相变材料（Phase Change material,PCM）的温控组件（Thermal Control Component,TCC）对航天器上的有效载荷进行温度控制。通过对载荷的温控需求分析,设计并制备了以Ga-Sn合金为PCM的TCC,并通过地面模拟实验对TCC的温控性能进行测试。实验结果表明这种含有Ga-Sn合金的TCC满足载荷的温控需求。最后在仿真软件中建立了TCC的相变传热仿真模型用于预测TCC的温控性能。结果表明：仿真模型计算所得结果与实验结果基本一致,可用于预测TCC的温控性能。     

TC4-DT钛合金磨削表面特性及其摩擦磨损性能

钛合金是一种典型难磨削加工材料,磨削表面易出现烧伤、裂纹等热损伤。本文开展了TC4-DT钛合金磨削实验,通过扫描电镜（SEM）、能谱（EDS）、X射线衍射（XRD）、显微硬度仪、金相显微镜及球-盘摩擦磨损实验仪研究了其表面特性及摩擦磨损性能。结果表明：低速磨削表面质量好,摩擦磨损性能较基体略提高;当砂轮线速度为80 m/s时,磨削表面质量良好,摩擦系数为0.38,较基体降低40%;而砂轮线速度为100 m/s时,磨削表面出现严重烧伤、网状裂纹。因此选择合理的高速磨削工艺可避免烧伤、裂纹等热损伤缺陷,并可有效改善表面摩擦磨损性能;磨削表面干摩擦磨损机制为磨粒磨损、粘着磨损和剥层磨损。     

低合金钢管的焊接工艺及缺陷预防

采用氩弧焊打底,焊条电弧焊填充盖面焊接Cr5Mn低合金钢管,钢管壁厚为12mm,焊接位置为水平固定全位置焊接,在焊接之前,调整好焊接工艺参数,焊接完毕以后,对焊缝外观检验和X射线无损检测,发现焊缝的表面出现少量微裂纹,内部有少量气孔。为了保证焊缝的质量,对缺陷产生的原因进行分析并且采取正确的焊接工艺方法避免焊接缺陷。     

基于Deform软件二次开发和BP神经网络的TA15多向锻造微观组织预报

通过热压缩实验构建了TA15合金的热变形真应力-应变曲线,以此为基础分别建立了合金双相区及单相区温度区间的热变形本构方程;基于热压缩试样动态再结晶的统计数据建立了TA15合金的动态再结晶模型。借助Deform提供的二次开发功能实现相关数学模型的程序化,制定正交实验方案,实现了TA15合金多向锻造变形的微观组织仿真。通过正交实验分析得出各项因子的影响对象及强弱差异,提出了双相区及单相区温度区间内的多向锻造最佳因子组合。建立了TA15合金多向锻造变形微观组织的BP （Back Propagation）神经网络预测模型,将预测结果与有限元仿真结果进行比较,结果表明两种方法的预测结果基本一致,但神经网络具备有限元仿真难以实现的良好细节预测能力,能更为细致地实现对微观组织分布状态的划分。     

退火温度对Al-Mg 合金拉伸性能和显微组织的影响

通过硬度、拉伸性能测试和金相组织观察,研究了不同退火温度对含和不合Sc的Al-Mg合金组织和性能的影响.结果表明:添加Sc明显提高了Al-Mg合金的强度,抑制了合金形变组织的再结晶,高温退火后1570合金中仍弥散分布的Al3( Sc,Zr)粒子质点造成其较高的再结晶温度及拉伸性能.     

TC1钛合金蜂窝夹层结构的钎焊工艺研究与分析

研究了TC1钛合金蜂窝夹层结构试件的钎焊工艺,通过对系列工艺下钎焊界面组织进行观察得出,在930℃/保温15min和一定钎料添加量的条件下,界面析出了TiNi2(Cu,Zr)化合物,且尺寸细小、分布弥散,因而相应钎焊试件的室温拉脱强度平均值较高,可达17MPa。在钎焊过程中,Cu和Ni元素由钎料向母材扩散,使母材β相变温度降低,导致界面魏氏体组织的产生;芯体波纹带间受钎料熔化热影响较大,导致此处魏氏体组织粗大,成为试件的薄弱部位。     

铣削参数对薄壁叶片铣削振动的影响

针对TC11薄壁叶片在数控加工过程中存在振动问题,采用单因素试验法进行薄壁叶片的铣削试验,建立铣削参数对振动加速度的影响模型,分析各铣削参数对铣削振动的影响规律,运用工艺参数区间敏感性分析方法,优选了铣削工艺参数区间。     

7050铝合金搅拌摩擦焊接头组织特征研究

针对7050铝合金搅拌摩擦焊接头,给出各组织特征区的定义,并对各特征区的组织状态、晶粒大小、沉淀强化相分布等进行深入的分析。为同材质的铝合金搅拌摩擦焊接头的综合性能评估提供更好的依据。